Ppsu P 3010 MR SW 10101,耐化学性良好, 粘度高, 阻燃
Ultrason® P 3010 MR SW 10101
聚苯砜
BASF Corporation
Technical Data
产品说明
Unreinforced, higher viscosity injection moulding grade, flame retardant and with improved chemical resistance.This grade is black colored and demolding optimized. Abbreviated designation according to ISO 1043-1: PPSU.
Physical form and storage:
Ultrason® pellets are supplied in bags and/or octabins. The bulk density ranges between 700 and 800 g/l. Provided the packaging remains undamaged, Ultrason® can be stored indefinitely. Ultrason® pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 4h at 130 °C to 150 °C in a vacuum or dry air drier prior to processing.
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • BASF Corporation
• Ultrason® P
供货地区 • 欧洲
添加剂 • 脱模
性能特点 • 耐化学性良好 • 粘度高. 阻燃
• 脱模性能良好 • 阻燃性能
机构评级 • EC 1907/2006 (REACH)
RoHS 合规性 • RoHS 合规
外观 • 黑色
加工方法 • 注射成型
部件标识代码 (No Standard) • PPSU
树脂ID (ISO 1043) • PPSU
物理性能 额定值单位制 测试方法
密度 1.29g/cm³ ISO 1183
溶化体积流率（MVR） (360°C/10.0 kg) 20.0cm³/10min ISO 1133
收缩率 3 ISO 294-4
横向流量: 23°C 1.0%
流量: 23°C 0.90%
吸水率 ISO 62
饱和, 23°C 1.2%
平衡, 23°C, 50% RH 0.60%
粘数 4 71.0cm³/g ISO 307
机械性能 额定值单位制 测试方法
拉伸模量 (23°C) 2270MPa ISO 527-2
拉伸应力 (屈服, 23°C) 74.0MPa ISO 527-2/50
拉伸应变 (屈服, 23°C) 7.8% ISO 527-2/50
冲击性能 额定值单位制 测试方法
简支梁缺口冲击强度 ISO 179/1eA
-30°C 24kJ/m²
23°C 60kJ/m²
简支梁缺口冲击强度 ISO 179/1eU
-30°C 无断裂
23°C 无断裂
硬度 额定值单位制 测试方法
球压硬度 (H 358/30) 124MPa ISO 2039-1
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 196°C ISO 75-2/A
玻璃转化温度(DSC) 5 220°C ISO 11357-2
Ultrason® P 3010 MR SW 10101
聚苯砜
BASF Corporation
热性能 额定值单位制 测试方法
线形膨胀系数 - 流动
23 到 80°C 0.000055cm/cm/°C ISO 11359-2
180°C 0.000062cm/cm/°C DIN 53752
注射 额定值单位制
干燥温度 130 到 150°C
干燥时间 4.0hr
加工（熔体）温度 350 到 390°C
模具温度 140 到 180°C
|